value.  The  assessment  is  carried  out  by  treating  a  fresh  concrete  chip  with  pH  indicators.  1% 

alcoholic solution of phenolphthalein changes color from colorless (pH = 9.3) to crimson (pH = 

10.5); 0.1% aqueous solution of alizarin red - from yellow (pH = 10.1) to lemon (pH = 12.1). 

A  minute  after  the  application  of  the  indicator  solution,  measure  the  depth  of  concrete 

neutralization with a ruler with an accuracy of 1 mm. 

The  depth  of  penetration  of  chlorine  ions  is  determined  by  wetting  a  fresh  fracture  of  concrete 

with a 1% solution of silver nitrate. Turbidity of the solution indicates the presence of chlorine 

ions in the concrete (more than 0.3% of the mass of cement). 

The depth of destruction of concrete under the influence of liquid acidic media is determined by 

removing the corroded layer with a sharp tool. 

The degree of corrosion of the reinforcement is assessed by the nature of the corrosion products 

(solid,  pitting, spots,  thin coating, layered, color and density), the area of  surface damage (as  a 

percentage  of  the  total  exposed  surface)  and  the  depth  of  corrosion  damage.  The  latter  is 

determined with relatively uniform corrosion by the difference (average) of the design and actual 

diameters of the reinforcement, divided by 2; in case of pitting corrosion, the depth of the ulcers 

is measured with an indicator needle. If the surface of the shaft is lined with a large number of 

ulcers,  the  initial  position  of  the  indicator  hand  can  be  set  using  a  calibrated  plate  (such  as  a 

safety razor blade) placed on the sample surface. 

For a quantitative assessment of the size of corrosion of the reinforcement, the reinforcement is 

opened in 10 structures of the same type, at least in the most corroded sections with a length of 1 

m.At  each  of  such  sections,  the  retained  diameter  of  the  reinforcement  is  measured  in  three 

places after removing the corrosion products of steel mechanically, for example, using an emery 

wheel, until a smooth, shiny steel surface is obtained. 

Opening  of  prestressed  reinforcement  (outside  the  anchorage  zone)  can  be  allowed  if  the 

operational  loads  have  extinguished  or  significantly  weakened  the  concrete  compression  forces 

created by prestressing, which, in particular, may be evidenced by the appearance of transverse 

cracks  in  the  area  of  the  prestressed  reinforcement  or  element  deflection.  and  also  after  the 

implementation of the appropriate safety measures. 

UKB-1m  device:  Measures  the  speed  of  propagation  of  an  acoustic  pulse,  the  change  in  its 

energy  and  frequency-amplitude  spectrum.  The  accuracy  of  measuring  the  amplitude  of  the 

pulses depends on the reliability of the acoustic contacts of the probes of the device and concrete, 

therefore,  along  with  the  attenuation  coefficient,  the  nature  of  the  reverberation  process  in  the 

section  of  the  element  is  also  determined.  When  inspecting  massive  reinforced  concrete 

structures at low frequencies (20-150 kHz), the sensitivity of the devices is low. However, some 

specific  defects  and  damage  caused  by  poor-quality  concrete  placement,  exposure  to  high  and 

low temperatures, corrosion, are easily detected. 

The  areas  of  the  damaged  layer  are  shown  by  the  fracture  of  the  longitudinal  hodograph  line 

(Fig. 2). The thickness of the modified surface layer is found by the formula: 



 



2

1

2

1

5

,

0

V

V

V

V

l

t

a

d









                         (10) 

Where: 

a

l

-  isthedistancefromtheemittingtransducertothebreakpointofthehodograph; 

1

V

 and 

2

V

 - 

respectively,the speed of ultrasound in undamaged and damaged concrete layers. 

---