9.8.2 Mechanical Stacks
A high-efficiency result may also be obtained by a mechanical stack, relaxing the need to
consider lattice matching. The most probable candidates for this are GaInP/GaAs stacked

---

FUTURE-GENERATION SOLAR CELLS
405
over either GaInAsP (1 eV)/GaInAs (0.75 eV) or GaSb [142, 143]. The difficulties in
implementing these stacks are associated with making the upper cell very transparent to
the sub–band gap light (use of a transparent GaAs substrate, nonconventional approach
for the back contact, and a good AR coating on the back, as well as the front, of the
upper cell) and with finding a way to mount both cells with simultaneous heat sinking
and electrical isolation, a much greater problem at 500 to 1000X than at 10 to 50X.
An advantage of this approach is the decoupling of the photocurrents of the two pieces
(assuming that four-terminal measurements are made), allowing for greater flexibility in
the choice of materials and higher efficiency when the spectrum is changed [99].
The efficiency of a solar cell depends on the operating conditions, complicating
the prediction of outdoor performance of solar cells. This is especially complicated for
series-connected, multijunction solar cells under variable spectra. The losses expected for
two-terminal operation of three- and four-junction cells, compared with six- or eight-
terminal operation of the same cells are significant, but may not be much more than the
loss that a silicon cell experiences by operating at elevated temperature [29]. For two-
terminal operation, the mechanical stack may most easily be accomplished by bonding
the two semiconductor materials directly. Because wafer bonding is now routinely used
for integrating many devices, techniques are available, and the wafer bond avoids the
need to use a transparent substrate, avoids reflection losses, and removes the difficulty
of heat sinking and electrically isolating the stacked cells. If a method for reusing the
substrate can be made economical, wafer bonding also has the potential to reduce the
substrate cost.
There are many more approaches to making a multijunction cell than can be dis-
cussed in this chapter. All approaches are variations on the structures shown in Figure 9.4.
Wafer bonding of III-V multijunction cells to silicon would provide a lighter substrate
(an advantage for space cells) and could reduce the cost if the original substrate could be
reused. A method for making a GaAs-Si bond with ohmic character between a GaAs cell
and a silicon wafer has been reported [144]. Wafer bonding has not yet been developed
for high-yield manufacturing of solar cells, but large-area wafer bonding is a possibility
given that eight-inch wafer-bonded silicon-on-insulator substrates are commercially avail-
able. The cost of these wafers is currently high (comparable to the cost of four-inch Ge
wafers), but may be reduced in the future.