Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

5.3.2.1  Historical slag 
The amount of Cu leached within 24 h was 214.7 mg/kg and 83.7 mg/kg for ARE at an initial 
pH 2.9 and 4.4, respectively (Table 5.2, Figure 5.2). A prolongation of the leaching time up to 
960 h led to  mobilization up to  803.1 mg/kg  and 302.0 mg/kg of Cu for ARE (pH 2.9) and 
ARE (pH 4.4), respectively. The amounts of Cu leached out from HS under exposure to HA 
and  FA  were  similar  to  values  extracted  by  ultrapure  water.  As  much  as  41.9  mg/kg  (HA), 
55.4  mg/kg  (FA)  and  37.5  mg/kg  of  Cu  (UPW)  was  mobilized  within  24  h  and  rose  up  to 
126.7  mg/kg,  130.0  mg/kg  and  97.7  mg/kg  after  960  h  of  leaching  (Table  5.2,  Figure  5.2). 
Similar trends of HS behavior could be observed for Zn and Pb. The quantity of Zn mobilized 
within 24 h was 118.6 mg/kg (ARE pH 2.9), 61.5 mg/kg (ARE pH 4.4), 7.6 mg/kg (HA) and 
9.3  mg/kg  (FA).  An  extension  of  the  leaching  time  up  to  the  960  h  led  to  release  of  79.6 
mg/kg  (ARE  2.9),  90.3  (ARE  4.4),  13.7  mg/kg  (HA)  and  11.7  mg/kg  (FA).  Amount  of  Zn 
leached out by UPW did not exceed 14.0 mg/kg throughout the experiment. The amount of Pb 
extracted by ARE over 24 h-960 h was maximally 23.0 mg/kg and 4.9 mg/kg for 2.9 and 4.4 
initial  solution  pH,  respectively.  The  amount  of  Pb  released  under  exposure  to  HA,  FA  and 
UPW did not reach values higher than 0.4 mg/kg (Table 5.2).