Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

TABLE 5.1 Chemical composition of slags.  
 
 
HS 
SFS 
GS 
LS 
Cu  [mg/kg]  5657  2687  11425  10915 
Zn  [mg/kg]  3962  3832  7810 
76400 
Pb 
[mg/kg]  111 
1559  21135  26125 
(HS: historical slag, SFS: shaft furnace slag, GS: granulated slag, LS: lead slag) 
 
 
5.2.2  Leaching solutions 
Leaching  experiments  were  performed  using  humic  (HA)  and  fulvic  acids  (FA)  as  well  as 
artificial root exudates (ARE). The HA and FA solutions were prepared by dissolving 20 mg 
of  commercial  (Suwannee  River,  International  Humic  Substances  Society)  humic  (HA)  or 
fulvic acid (FA) in 1 L of MilliQ water (20 mg/L) and were pre-set at initial pH of 4.4.  
The ARE solution  corresponded to  the rhizosphere  composition  described by  Baudoin  et  al. 
(2003) and contained:  glucose (3.31 g/L), fructose (3.31 g/L), sucrose (3.15 g/L), citric acid 
(1.77  g/L),  lactic  acid  (1.66  g/L),  succinic  acid  (1.63  g/L),  alanine  (0.74  g/L),  serine  (0.97 
g/L)  and  glutamic  acid  (0.81  g/L).  The  initial  pH  of  ARE  solution  was  2.9  and  4.4  for  two 
different treatments. The pH value of the solutions was adjusted using HNO
3 
or NaOH. 
The  ARE  solution  is  composed  of  simple,  low  molecular  weight  organic  acids,  whereas 
HA/FA are characterized by a more complex structure and higher molecular weight (Schulten 
& Schnitzer, 1993). 
 

---

CHAPTER 5: METAL MOBILIZATION FROM Cu-SLAGS BY SOIL ORGANIC ACIDS
 
 
140