Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

v) Alteration of slags (Scanning electron microscopy) 
Slag  samples  resulting  from  treatments  with  the  organic  solutions  were  observed  by  SEM 
with  respect  to  presence  of  weathering  features.  At  the  end  of  the  experiments,  grains  were 
dried  and  coated  with  Au.  Microscopic  observations  of  slags  were  conducted  using  SEM 
(JEOL  JSM-601OA)  coupled  with  an  Energy  Dispersive  Spectrometer  at  high  vacuum  and 
15-20 kV working mode. 
At the end of bio/weathering experiments, slags grain were observed with respect to surface 
changes  using  Scanning  Electron  Microscope  (QEMSCAN  650F)  at  10-20  kV  and  high 
vacuum working mode. 
Slags from  abiotic and biotic leaching experiments were examined with respect to alteration 
features  resulting.  Dried  slag  grains  were  coated  with  Au  and  mineralogical  analysis  was 
performed  under  SEM  equipped  with  Energy  Dispersive  Spectrometer  (EDS)  (JEOL  JSM-
601OA) at high vacuum and 15-20 kV working mode.