Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-converter 
slag 
 
Fe: 38.82% 
Cu: 4.03% 
Co: 0.48% 
Ni: 1.98% 
Bioleaching culture: Aspergillus niger 
Medium: potato dextrose, pH 6.8 
 
FS: <150 µm 
L/S: 10 – 50 
T: 37°C 
LT: 72 h 
AS: 120 rpm 
 
Abiotic experiments: acetic, succinic, oxalic acids (1 
M) 
Control: distilled water 
 

 
Considerable  decrease  in  metal  extraction  observed  along  with  increased 
pulp  density  (L/S  50:  Cu  47.14%  (19  g/kg)  «,  Co  49.87%  (2.4  g/kg),  Ni 
23% (4.6 g/kg), Fe 4.2% (16.3 g/kg), L/S 10: Cu 7.3% (2.9 g/kg), Co 5.4% 
(0.3 g/kg), Ni 2.5% (0.5 g/kg), Fe 1.2% (4.7 g/kg)) 

 
Increasing dextrose concentration was favourable for microbial activity and 
increased metal extraction (Cu 78.5% (31.6 g/kg) #, Co 90% (4.3 g/kg), Ni 
45.5% (9 g/kg), Fe 40.15% (155.9 g/kg)) 

 
Indigenous  microorganisms  are  recommended  for  leaching  process  due  to 
their well-developed metal tolerance 

 
Tolerance  of  microbes  for  metal  for  leaching  purpose  may  be  developed 
through enrichment of medium that they grow in 

 
Abiotic experiment revealed stronger effect of succinic acid than oxalic one 
(succinic  acid  Cu  ~50%  (~20.2  g/kg),  Co  ~100%  (~4.8  g/kg),  Ni  ~40%, 
Fe~60%  (~232.9  g/kg);  oxalic  acid:  Cu  ~6%  (2.4  g/kg)  and  Co  ~6%  (0.3 
g/kg),  Ni  0%,  Fe  20%  (77.6  g/kg)).  Acetic  acid  shows  comparable,  but 
slightly lower effect than succinic acid 
Sukla et al. 
(1995) 

---

CHAPTER 2: COPPER METALLURGICLA SLAGS- CURRENT KNOWLEDGE AND FATE:  
A REVIEW
 
 
62