Automotive Coatings Formulation: Chemistry, Physics und Practices

 
film thickness 30 % higher than the average 
application layer thickness 
[107]
. 
Popping
is the formation of blisters due to the sudden evaporation of solvent or reaction products 
(a boiling process on small film spots). These defects are observed particularly when evaporation 
occurs at a stage when the surrounding film has already achieved higher viscosities through 
evaporation and crosslinking reactions. The popping tendency is also determined with the aid 
of a wedge-shaped paint layer 
[108]
. The application conditions are chosen so as to promote pop-
ping. Parameters that influence popping are, in addition to layer thickness, the amount applied 
per time (transfer masses), the air temperature, the air-fall velocity (the rate of air circulation in 
the flash-off zone) and finally
 
the temperature curve in the stoving oven. Popping may also occur 
when air is introduced into the paint material during the production process, either in dissolved 
form or as micro-foam, and then escapes during film forming. Therefore, the specific application 
conditions which vary from one application line to the next, must be taken into consideration for 
specific paint formulations. Thus, the composition of topcoats of the same colour may vary with 
the application line on which they are used. Parameters that can be used to influence the popping 
tendency are solvent composition, application solids content, application viscosity, and the reac-
tivity of the resins for crosslinking, including the type and quantity of catalysts. Since reactivity 
is very high, the film viscosity increases rapidly in the first stoving phase. If, after that,
 
further 
reaction products are cleaved, they may give rise to blisters (reaction blisters). 
Levelling
, too, is significantly influenced by the application conditions. For optimum levelling, 
the spray particles must wet the surface perfectly, spread over the surface and flow together to 
form smooth, homogeneous films. Evaporation of solvents in the flash-off zone and at the start 
of stoving creates convection currents in the paint layer which may impair the film smoothness. 
These processes differ in vertical and horizontal film layers. Nonetheless