Asian Research Journals

Asian Research Journals
 
 
 http://www.tarj.in 
 
160 
 
Special 
Issue 
acetylene,  VA,  acetaldehyde).  Reactions  such  as  decomposition  of  zinc  acetate,  decomposition 
of acetic acid, leading to the formation of volatile products, can hardly cause a decrease in coal 
activity. 
The study of the effect on the catalyst of various components of the gas mixture (acetylene, vinyl 
acetate, acetic acid, acetaldehyde), as well as nitrogen, showed that the effect of the components 
of  the  mixture  on  activated  carbon  is  much  weaker  than  on  the  contact  mass.  Acetylene  and  a 
mixture  of  acetylene  with  vinyl  acetate  have  a  very  strong  effect  on  the  catalyst.  No  harmful 
effect of acetaldehyde on the contact mass was observed. Vinyl acetate mixed with nitrogen has 
virtually no effect on both activated carbon and contact mass. Nitrogen added to the gas mixture 
has a beneficial effect on the life of the catalyst, but slightly reduces the conversion. 
To clarify the effect of impurities to acetylene on the initial activity of the catalyst, the reaction 
was carried out with acetylene obtained by the action of water on technical calcium carbide. This 
acetylene without further purification entered the drying system with calcium chloride and then 
through  the  evaporator  into  the  contact  zone.  For  comparison,  an  experiment  was  carried  out 
under similar conditions with carefully purified acetylene. 
The  use  of  crude  acetylene  did  not  have  a  significant  effect  on  the  initial  conversion  of  acetic 
acid.  The  presence  of  a  sorption-active  surface  in  the  reaction  zone  can  cause  sorption  by  the 
contact mass of ordinary impurities to acetylene and thereby reduce the effect on their reaction to 
a  certain  limit.  Therefore,  it  is  possible  to  assume  that,  after  prolonged  contacting,  crude 
acetylene can have a harmful effect on the catalyst. The life expectancy of the catalyst depends 
on the mode of operation. 
The texture characteristics of nanocatalysts based on the sol-gel technology are presented in table 
- 1.