Asian Journal of Multidimensional Research (ajmr)

40% microfill (ash TPP) 

RESULTSANDDISCUSSION 

Analysis  of  the  available  data  indicates  an  increase  in  the  activity  of  cement  binder  in  the 

presence of 0.002% Poly-ans-2 additives by 15%. 

---

ISSN: 2278-4853         Vol 10, Issue 9, September, 2021        Impact Factor: SJIF 2021 = 7.699 

Asian Journal of Multidimensional Research (AJMR)

 

https://www.tarj.in

 

561 

 

AJMR 

The optimal compositions  of cement binders obtained with  different  contents  of micro-filler 

(ash TPP) according to [4] are shown in table 1. 

TABLE 1OPTIMUM CEMENT BINDERS 

 

№ 

 

Components  of  cement-ash  binder  with  an  optimal 

grinding time of 45 min 

Compressiv

e  strength, 

МPа, R* 28 

W*/

W 

1).Portland 

cement clinker, 

% 

2)   gypsu

m block, % 

Ash, 

% 

3) additive 

Poly-ans-2, 

% 

1 

82,0 

3 

15 

0,002 

75,9

х)

 

0,220 

2 

72,4 

2,6 

25 

0,002 

77,6

х)

 

0,225 

3 

57,9 

2,1 

40 

0,002 

67,2

х)

 

0,245 

4 

38,6 

1,4 

60 

0,002 

37,6

х)

 

0,285 

 

1) Tested halves of beams 4x4x4 cm in size (number of samples 3); 

2) The optimum amount of gypsum stone was found to  be 3.5% by weight  of Portland cement 

clinker; 

3) The optimal amount of Poly-ans-2 additive is determined by the weight of the binder. 

The  performed  design  of  the  optimal  compositions  of  cement  binders  for  corrosion-resistant 

concrete according to the general method of the ISC theory allows us to  determine the optimal 

region of structures with high quality characteristics in the range of water-binders and to select 

the most rational one from them [8-25]. 

CONCLUSIONS 

Thus, by increasing the fineness of grinding, it is possible to increase the activity of the cement-

ash  mixed  binder,  and  based  on  the  dependence  of  the  latter  on  the  dosage  of  ash  and  the 

duration of grinding (Fig.3,4) it is possible to allocate three groups of the binder:    

1.

 

-  with  ash  dosage  up  to  20%,  when  the  activity  of  cement-ash  binder  practically  does  not 

differ from the original additive-free cement at the same energy costs for grinding; 

2.

 

 -  with  a  dosage  of  ash  from  20  to  40-50%,  when  there  is  a  proportional  decrease  in  the 

activity of the binder and then in this range it is rational to compensate for the decline in the 

strength of the binder by increasing the dosage of ash by increasing the fineness of grinding; 

3.

 

  - with a dosage of ash more than 50%, when there is a noticeable decrease in the activity of 

the  binder,  and  the  latter  is  difficult  to  compensate  for  the  increase  in  the  fineness  of  the 

binder due to the increase in the duration of grinding.   

4.

 

-An  increase  in  the  activity  of  the  mixed  binder  was  found  due  to  the  introduction  of  a 

gelpolymer additive into the composition during grinding of the binder [10,11]. The reagent 

polymer  polyacrylonitrile  hydrolyzed  stabilizing  was  used.  In  the  course  of  preliminary 

experiments,  it  was  found  that  the  greatest  effect  is  achieved  when  it  is  introduced  in 

hundredths of the mass of cement. On the basis of the above, it follows that the methods of 

determining  the  activity  of  cement  by  the  General  method  of  designing  the  optimal 

composition  of  CONCRETE  serve  as  a  tool  for  operational  control  of  the  technological 

---

ISSN: 2278-4853         Vol 10, Issue 9, September, 2021        Impact Factor: SJIF 2021 = 7.699