Actual problems of modern science, education and training

Synthesis of copper nanoparticles using “HF”. We used an aqueous solution 
of “HF” as a stabilizer in the synthesis of copper nanoparticles. We used an aqueous-
alcoholic solution of calcium chloride to obtain an aqueous solution[15] of “HF”. We 
poured 50 ml of 0.001 g / ml “HF” solution into a 250 ml volumetric conical flask. We 
added  5  ml  of  0.005  M  copper  (II)  sulphate  solution  to  the  solution  by  stirring  the 
solution in the flask for 10 min at 500 rpm using a magnetic stirrer. The solution was 
then added from an alkaline solution until the solution temperature was 363 K and the 
solution medium was pH=11–14. Once the pH had reached the specified value, 2 ml 
of the solution in a 0.5 M solution of ascorbic acid was added dropwise to the mixture 
in the flask and held at 800 rpm for 30 min. As a result of the process, the solution 
turned red. 
A similar experiment was performed at a temperature of 333-353K. But at the 
end  of  the  process,  the  solution  turned  yellow.We  analyzed  the  solution  by  UV-
spectroscopy.